退火工艺对钛阳极用1.0 mmTA1钛卷组织和性能的影响

Effect on Microstructure and Properties of Annealing Process for Titanium Anode with 1.0 mm TA1 Titanium Coil

    摘要
  • 摘要: 采用不同的退火工艺对冷轧TA1钛卷进行罩式炉退火处理，对比分析不同退火工艺下的微观组织和力学性能。结果表明：在相同保温时间下，冷轧钛卷在630 °C和650 °C保温退火，组织为完全再结晶等轴组织，且650 °C退火温度晶粒尺寸发生明显的长大。相同的退火温度下，晶粒尺寸随着保温时间的增加而明显的长大。通过选择合理的退火工艺630 °C/10 h，TA1钛卷可获得良好的力学性能和晶粒度匹配性，满足钛阳极板和网的特殊要求。

     